HALOX®
350
Organic Corrosion Inhibitor
Typical Properties
These are typical values and do not represent product specifi cations:
pH (10 wt% sol)
Active solids
Appearance
Density (g/ml) 1.57
Melting point
3.3
97-100%
Slightly yellow powder
1.57
Approx. 170°C (decomposition)
Revised 2/6/18
Our Manufacturing Systems are ISO 9001 and ISO 14001 Certi! ed
Incorporation
A pre-neutralized solution of HALOX® 350 in water should be prepared using an amine that is volatile under your curing conditions,
then post-add or add to the letdown.
A neutralization example:
HALOX® 350 (30% solution)
De-ionized Water
28% Ammonium Hydroxide
HALOX® 350
Total:
Stir slowly, adjust to pH 8-9
Weight
53.0
19.0
27.7
100.0
In general, add the aqueous concentrate to the amine/amide part of a 2 pack epoxy or to the polyol of a 2 pack polyurethane.
If possible, avoid systems with acetic acid. Use surfactant stabilized hardeners instead.
Check compatibility, shelf life (e.g. accelerated at high temperature), cure and pot-life, if applicable. Other formulation variables may
also be optimized, for example, dispersants, surfactants, and PVC: CPVC ratio |